Blood Collection PET Tube Resin

APPLICATIONS

Medical test tubes, such as medical vacuum blood collection tubes

FEATURES

  • Copolymer resin with a nominal intrinsic viscosity of 0.57dl/g.

  • Specially designed to have high melt flow capability, inhibited crystallization rate, and high transparency for injection process, which is especially suitable for pharmaceutical test tubes such as blood collection tubes which require mechanical, gloss, and brightness properties

  • Produced in a state-of-the-art continuous polymerization technology and is combined with a strict quality monitoring system.

  • Conforms to FDA Regulation 177.1630

  • Totally recyclable

MODELS

Resin production facilities are in compliance with ISO 9002, ISO 14001, OHSAS 18001, and U.S. FDA management regulations

ISO 14001 Icon
FDA Icon

3572 Specifications

Item
Unit
Value
Testing Method

Intrinsic Viscosity

dl/g

0.57 ± 0.02
ASTM D4603

Melting Temperature

°C

224 ± 3
ASTM D3418

Moisture

%

≦0.30
Nan Ya Method

Chip Size

chips/2g

130 ± 3
Weight Scale

Hunter L Value

-

85.0 ± 2.0
ASTM E1164

Hunter b Value

-

-4.0 ± 1.0
ASTM E1164

Fines

ppm

<100
Nan Ya Method

Tensile Strength

MPa

57.8
-

Elongation

%

5.2
-

Flexural Strength

Mpa

90.9
-

Flexural Modulus

Mpa

2460
-

Impact Strength

Kg cm/cm

3.3
-

Rockwell Hardness

R

106
-

Shrinkage

%

0.8
-

Suggestions

Processing Type: Injection molding, Drying Temperature: 140~160°C, Drying Residence: 2~4 hr, Screw Temperature: 260~290°C, Suggest to cooperate with Nan Ya Nucleating Masterbatch (5~10%)

Expiration Date

Consume PET resin within 1 year from pack date

Storage Conditions

Store PET bag in a dry and clean warehouse

The technical data sheet is for reference only, the actual data depends on the delivery quality inspection report (COA)

3642 Specifications

Item
Unit
Value
Testing Method

Intrinsic Viscosity

dl/g

0.615 ± 0.02
ASTM D4603

Melting Temperature

°C

245 ± 5
ASTM D3418

Moisture

%

≦0.30
Nan Ya Method

Acid Value

10⁻⁶equ/g

30 ± 10
Nan Ya Method

Chip Size

chips/2g

130 ± 3
Weight Scale

Fines

ppm

<100
Nan Ya Method

Hunter L Value

-

85.0 ± 2.0
ASTM E1164

Hunter b Value

-

-3.5 ± 1.0
ASTM E1164

Suggestions

Processing: Injection molding, Drying Temperature: 140~160°C, Drying Residence: 2~4 hr, Screw Temperature: 260~290°C, Suggest to cooperate with Nan Ya Nucleating Masterbatch (5~10%)

Expiration Date

Consume PET resin within 1 year from pack date

Storage Conditions

Store PET bag in a dry and clean warehouse

The technical data sheet is for reference only, the actual data depends on the delivery quality inspection report (COA)