Extrusion Blow PET Bottle Resin

All Products / PET Resins / Bottle /

APPLICATIONS

Bottles with handles, packaging of contents such as food, beverages, high thickness cosmetic bottles, detergent, and water filter housings

FEATURES

Copolymer resin with a nominal intrinsic viscosity of 1.05dl/g.
Designed for the extrusion blow molding process. Therefore, this resin possesses high melt strength to prevent the drawdown of its molten parison
Offers the excellent clarity and sparkle needed for clear articles
Applications include extrusion blow-molded containers, extruded film and sheet, and profiles, especially able to convert ed into an integrated handled clear bottle
Suitable replacement material for PVC, which is far less recyclable
Suitable replacement material for HDPE, which could not be a clear article. It has better chemical resistance than PETG material
Produced in a state of the art continuous polymerization technology and is combined with a strict quality monitoring system
Conforms to FDA Regulation 177.1630
Totally recyclable
Bottles made from P115 are classified as the No. 1 plastic material

MODELS

Resin production facilities are in compliance with ISO 9002, ISO 14001, OHSAS 18001, and U.S. FDA management regulations

Item	Unit	Value	Testing Method
Intrinsic Viscosity	dl/g	1.10 ± 0.02	ASTM D4603A
Melting Temperature	°C	233 ± 3	ASTM D3418
Ash Content	%	≦ 0.02	Nan Ya Method
Moisture	%	≦ 0.30	Nan Ya Method
Acetaldehyde	ppm	≦ 1.0	Gas Chromatography
Acid Value	10⁻⁶equ/g	20 ± 10	Titration Method
Bulk Density	g/cm³	0.90 ± 0.05	JIS K-5101
Chip Size	chips/2g	150 ± 3	Weight Scale
Fines	ppm	＜100	Nan Ya Method
Hunter L Value	-	86.0 ± 2.0	JIS Z-8722
Hunter b Value	-	-1.0 ± 1.0	JIS Z-8722

Suggestions	Drying Temperature: 160~170°C, Drying Residence: 4~6 hr, Drying Dew Point: -40°C, Drying Air Flow: 1ft³/min/lb-PET, Mold Temperature: 240~265°C
Expiration Date	Consume PET resin within 1 year from pack date
Storage Conditions	Store PET bag in a dry and clean warehouse